分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-26
摘要: The microstructural features and the effect of Mo addition during incubation period in FeCrNi austenitic alloy were investigated using positron annihilation technique and micro-Vickers Hardness. The electron irradiation, which could induce vacancy defects in material, was performed at room temperature up to the dose of 1.70-4 and 50-4 dpa, respectively. The defect concentration was estimated about 10-4-10-7 though standard trapping model. The added Mo could trap vacancies to form Mo-vacancy complexes, which may suppress the migration and growth of vacancy defects during electron irradiation. In addition, the microstructural evolution during electron radiation resulted in hardening, while the added Mo might to improve the hardening property of the alloy.
分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-26
摘要: Abstract. The microstructural features and the effect of Mo addition in FeCrNi austenitic alloy during incubation period were investigated using positron annihilation technique and micro-Vickers Hardness. The electron irradiation, which could induce vacancy defects in material, was performed at room temperature up to the dose of 1.70-4 and 50-4 dpa, respectively. The defect concentration was estimated about 10-4-10-7 though the standard trapping model. The added Mo atoms could trap vacancies to form Mo-vacancy complexes, which may restrain the migration and growth of vacancy defects during electron irradiation. In addition, the microstructural evolution during electron radiation resulted in hardening, while the added Mo might improve the hardening property of the alloy.
分类: 物理学 >> 凝聚态:结构、力学和热性能 提交时间: 2017-03-23
摘要: The effect of isochronal annealing on vacancy-type defects in quenched FeCrNi alloys and SUS316 has been investigated by positron annihilation techniques. Vacancy-type defects gather and grow with the annealing temperature increasing to 523 K, and the vacancy-type defects annihilated gradually in FeCrNi alloys at the annealing temperature increasing. The results indicate that the addition of Mo and nonmetal elements is not the key reasons that determined the annihilated temperature of vacancy-type defects. It’s worth noting that the vacancy-type defects annihilated and dislocation-type defects formed in all sample alloys after 673 K annealing treatment. In addition, the density of defects in Mo diluted FeCrNi model alloy is lower than that in FeCrNi model alloy due to the Mo-vacancy complexes formed in Mo diluted FeCrNi model alloy. The long lifetime of vacancy-type defects in commercial stainless steel SUS316 is smaller than that in FeCrNi model alloys because the mobility of vacancy-type defects changed by nonmetal elements. In addition, vacancy-type and dislocation defects detected contribute to the S and W parameters of positron annihilation in the whole annealing treatment.